薄壁玻璃钢管DMC压制模的优化设计解决了偏心问题

薄壁玻璃钢管DMC压制模的优化设计
于丽君，周维智
(沈阳工学院，辽宁沈阳113122)
摘要:通过对薄壁玻璃钢管工艺特性分析，介绍了适合该薄壁玻璃钢管压制成型的特殊模具结构设计及工艺条件。同时通过三维造型、模拟试验，优化模具设计，解决了生产中薄壁管出现的偏心问题。
关键词:DMC压制料;薄壁玻璃钢管压制；模具设计
中图分类号:TQ171.635    文献标识码:B    文章编号：KXH-2168(2013)12-0064-03
Optimization design of DMC compression mould for thin-wall frp pipe
YU U-jun, ZHOU Wei-zhi
(Shenyang Institute of Technology, Shenyang, Liaoning 113122, China)Abstract: The structure £ind process conditions of a mould for the compression forming ofa thin-wall frp pipe were designed based on analysis of the technological performance of the pipe. The eccentric problem in the production of the thin-wall pipe was solved through 3D modeling, simulation experiment and optimization design of the mould.
Key words: DMC compressed material; compression of thin-wall frp pipe; mould design

1、引言
薄壁玻璃钢管用在耐压、耐温等控制元件的绝缘引出端，对同轴度要求较高，因为受增强纤维材料工艺性的制约而在压制过程出现一些影响产品
质量的现象，例如:偏心、壁厚不均、熔接痕、充填不满等缺陷。通过计算机三维造型、模拟试验可以优化模具结构，根据优化设计结果可以研制出适合批量生产的实用模具，解决现存的质量问题。
2、制件特征及工艺分析
2.1薄壁玻璃钢管的结构

图1为薄壁玻璃钢管三维图，图2为薄壁玻璃
钢管二维图。薄壁玻璃钢管比较简单,其质量要求是不允许有裂纹和变形缺陷，同轴度要求押.05 mm。
(1)    外形尺寸。塑件壁厚为0.75 mm，材料流动性不好，达到了塑件较小成型极限，选择压制成型。
(2)    精度等级。每个尺寸的公差不一样，有的属于一般精度，但是有同轴度的要求，一般按实际公差进行计算。
(3)表面质量要求。表面光滑无熔接痕，也不允许有浇口痕迹和变形缺陷。
2.2制件偏心产生原因
制件为细长薄壁，内孔仅为多3.5 mm，压制过程中材料受压流动产生侧向力对型芯施压,造成型芯弯曲，偏心不垂直。玻璃钢管http://www.gexingju.com